Gas Pipeline Coating Butyl Rubber Tape Anti Corrosion Pipe Tape High Performance

0.635mm black color 100width  high strength polyethylene butyl rubber tape for corrosion protection of gas pipeline 

ⅠSystem description:

The XUNDA-T-100 series is Cold applied tape coating system for corrosion protection of Oil, Gas, Petrochemical, and Waste Water underground or overhead pipelines.

The butyl rubber tape shall be applied after the Liquid adhesive and before the outer-layer tape by hand or with a wrapping machine

ⅡStructure:

The specification of the tape consists of two layers, adhesive layer and film backing

Adhesive: Butyl rubber

Film backing: Special blend of stabilized polyethylene

Ⅲ Features:

Excellent adhesion to pipe and self

Can be applied over a wide temperature range

Good conformability and consistent uniform thickness              

Easily applied with no special equipment

Compatible with common pipe coatings              

Excellent resistance to cathodic disbonding

Meets ASTM D 1000 Standard

Cold applied

Ⅳ Physical Properties

 Polythene Butyl tape (inner layer)

 Cold applied coating tape Application Instruction

1.Steel pipe pretreatment

1.1 Keeping the pipe external surface clean and dry. Remove the dust,

oil, welding slag, burrs, grease and dirt on pipe surface.

1.2 Pipe surface prepared up-to a level of Sa 2 or 2 ½ or St 2/st by sand blasting.

1.3 After the pre-cleaning operations, the pipe surface not smooth

which may sharp the pipe coating should be burnished , the abrasive

dust attached on the pipe surface should also be cleaned clearly.

1.4 If flash rusting occurs, the surfaces must be re-cleaned by blasting as above.

2.Coating &Wrapping application

2.1 Coating &wrapping application consist of primer application, inner

tape coating ,outer tape coating .

2.2 weather condition

2.2.1 When the wind&sand was strongly, when the sand and dust covered

on the surface of pipe, primer ,tape etc., should not be brushing primer

and wrapping the tape if there is no reliable preventive measures.

2.2.2 When air humidity is greater than 80%,or when the pipe surface is wet from any precipitation, should not be brushing primer and wrapping tape.

3.Brushing primer

3.1 The brushing time should be control within 6 hours between the pipe surface treatment and brush primer. During brush primer, pipe surface should be free from damp and pollution. If the pipe surface rust return, should be re-pre-cleaned.

3.2 The primer should be mixed evenly in the container before brushing.

3.3 The primer should be applied uniformly, without any sags, floods, runs, drips, bare spot and over spray, such as leakage brush, clot, streaming. The primer coat DFT shall not be less than 25-50micron (1-2mils)

3.4 After the primer dried, then wrapping the tape(It usually takes 3to 5 minutes.).

3.5 Consumption:

machine application                                      approx. 0,1 litre/m²

hand application                                            approx. 0,2 litre/m²

4.Wrap tape application

4.1 Wrap tape application consists of hand application and machine application.

4.2 The tape applied temperature must be above 5 degrees,the coating construction temperature shall be more than -5 degrees as better .

4.3 The tape shall be spirally applied ,minimum overlap shall not be less than 50%.

4.4 When a new roll of tape started ,the ends shall be located to ensure the continuity of wrap tape using the same method of application.

4.5 Outer tape applied method is the same as above.

5.Cutbacks

Cutbacks shall be a minimum 6inches(150mm) from the ends of each

pipe.The cutbacks may be tapered or straight edge for the total thickness

of the coating.